标题：Degradation of bisphenol A by activating peroxymonosulfate with Mn0.6Zn0.4Fe2O4 fabricated from spent Zn-Mn alkaline batteries

作者： Lin, H (Lin, Heng); Li, SM (Li, Simiao); Deng, B (Deng, Bin); Tan, WH (Tan, Weihua); Li, RM (Li, Ruimeng); Xu, Y (Xu, Yin); Zhang, H (Zhang, Hui)

来源出版物：CHEMICAL ENGINEERING JOURNAL 卷：364 页码：541-551 DOI：10.1016/j.cej.2019.01.189 出版年：MAY 15 2019

摘要： Spinel ferrites have shown great potential to activate peroxides for environmental remediation. In this work, a Mn-Zn ferrite catalyst was fabricated by the citrate combustion method from spent Zn-Mn alkaline batteries. The synthesized Mn0.6Zn0.4Fe2O4 catalysts were applied to activate peroxomonosulfate (PMS) and degrade bisphenol A (BPA) in water. A 95.8% BPA (0.1 mM) removal was achieved at initial pH of 6.2, Mn0.6Zn0.4Fe2O4 dosage of 0.2 g/L, PMS concentration of 0.5 mM, and reaction time of 60 min. The concentration of metal leaching and radical identification experiments suggested that BPA is mainly degraded by surface-adsorbed reactive radicals. Metals at A site of the spinel (AFe(2)O(4), A = Mn and Zn) were responsible for PMS activation and Fe(III) acted as the reservoir for the surface hydroxyl groups, which substantially accelerated the degradation of BPA. The addition of Cl- improved the destruction of BPA and a NaHCO3 concentration below 5 mM had a negligible effect on the BPA removal. When the PMS/Mn0.6Zn0.4Fe2O4 process was used to treat real river water spiked with BPA, the removal of BPA was much faster than that in deionized water. This implied that the PMS/Mn0.6Zn0.4Fe2O4 process may provide some new insights not only for the recycling of spent batteries, but also for removal of contaminants from wastewater.

入藏号：WOS:000458504800053

文献类型：Article

语种：English

作者关键词：Mn-Zn ferrite; Peroxomonosulfate; Spent Zn-Mn alkaline batteries; Bisphenol A

通讯作者地址：Zhang, H (通讯作者)，Wuhan Univ, Hubei Environm Remediat Mat Engn Technol Res Ctr, Dept Environm Sci & Engn, Wuhan 430079, Hubei, Peoples R China.

电子邮件地址：eeng@whu.edu.cn

地址：[Lin, Heng; Li, Simiao; Deng, Bin; Tan, Weihua; Li, Ruimeng; Xu, Yin; Zhang, Hui] Wuhan Univ, Hubei Environm Remediat Mat Engn Technol Res Ctr, Dept Environm Sci & Engn, Wuhan 430079, Hubei, Peoples R China.

影响因子：6.735